Question # 25

Where is the weld HAZ assumed to be for purposes of hardness testing?

A.

0.25 inch on either side of the fusion zone

B.

0.25 inch away from the toe of the weld into the base metal

C.

1 inch on either side of the centerline of the weld

D.

Just adjacent to the toe of the weld

Full Access
Question # 26

API Recommended Practice 2201 primarily covers the:

A.

WPS/PQR aspects of in-service welding.

B.

Technical aspects of hot tapping.

C.

Safety aspects of in-service welding.

D.

Weldability aspects of in-service welding.

Full Access
Question # 27

A crack with its major axis oriented approximately perpendicular to the weld axis is called a:

A.

Lamellar crack.

B.

Non-directional crack.

C.

Transverse crack.

D.

Perpendicular crack.

Full Access
Question # 28

Which of the following is a commonly accepted advantage of flux core arc welding (FCAW)?

A.

Equipment is simple, inexpensive, and portable.

B.

The slag supports and shapes the weld bead.

C.

There is a reduced requirement for ventilation.

D.

There is minimal postweld cleanup.

Full Access
Question # 29

The carbon equivalent formula indicates:

A.

Whether postweld heat treatment (PWHT) will be needed.

B.

Whether preheat will be needed.

C.

The theoretical carbon content of a steel.

D.

The weldability of a steel, based on carbon content.

Full Access
Question # 30

When performing a carbon steel to carbon steel hot tap where the CE of one of the metals is greater than 0.42%, which of the following electrodes should be used?

A.

E7048-H4

B.

E7048

C.

E7018-A1

D.

E7018

Full Access
Question # 31

Which term is used to describe a groove melted into the base metal adjacent to the weld toe or weld root and left unfilled by weld metal?

A.

Longitudinal groove

B.

Incomplete fusion

C.

Under fill

D.

Undercut

Full Access
Question # 32

Which of the following can result from residual magnetism left in a partially completed weld?

A.

Excessive distortion

B.

Tendency of weld pool to be sluggish

C.

Deflection of the weld arc

D.

Solidification cracking

Full Access
Go to page:

Hot Exams

ADM-201 Dumps
Platform-App-Builder Dumps
AZ-500 Dumps
350-701 Dumps
SY0-601 Dumps
NCSE-Core Dumps
PDP9 Dumps
DP-203 Dumps
AZ-700 Dumps
NSE7_EFW-7.0 Dumps
Integration-Architect Dumps
CS0-003 Dumps